High Strength Mold Making RTV-2 Silicone Rubber For Plaster
Concrete Mold Making
MCSIL-930 RTV2 silicone rubber is a kind of two-component material,
that is the mold making silicone rubber made up of Part A base
silicone and Part B curing agent. The mixed Part A base silicone
and Part B curing agent can cure at room temperature by a
condensation reaction,then become a silicone rubber mold that can
be used for objects reproduction.
FEATURES
・Good flow ability and long working time
・Medium hardness
・High tear and tensile strength
・Easy de-mould from complex replica parts
・Acid and alkali-resistance
・Low linear shrinkage
APPLICATIONS
MC Silicone MCSIL-930 suited for reproduction of plaster molding, figures, art objects,
decoration molding, GRC products, gypsum products, resin products,
PU molds, etc.
Technical Data
Item No. | Character before curing | Curing |
| Part A | Part B | Part A+ Part B | Pot life at 250C mins | De-molding Time at 250C hours |
| Appearance | Appearance | Ratio | Viscosity cps |
| RTV930 | White | Clear | 100:10 | 14000-16000 | 30-45 | 4-6 |
| Character after curing 24 hours |
Hardness Shore A | Tensile strength | Tear Strength | Elongation break (%) | Linear Shrinkage |
| 28-30 | 4.0 Mpa | 28 N/mm | 510 | ≤0.3% |
How to make the silicone mold?
- The surface of the original should be clean and free of loose
material. If your products with thin flower patterns, and
especially with porous substrates, please use a suitable mold
release agent such as soap water, detergent, Vaseline or petroleum
jelly.
- Mixing
Please weight 100 Part A base and 10 parts of CA30-10 Curing Agent
in a clean container. Thoroughly stir Part A base silicone before
use, as filler separation may occur upon prolonged storage. Mixing
Part A and Part B evenly until the CA30-10 completely dispersed in
the base. Hand or mechanical mixing can be used, but do not for an
extended period of time or allow the temperature to exceed 35C
(95F). Mix suitably small quantities to ensure thorough mixing of
base and curing agent.
Pouring the mixture and curing
Pour the mixed Part A base silicone and CA30-10 curing agent as
soon as possible onto the original, avoiding air entrapment. The
catalyzed material will cure to a flexible rubber within 8 hours
(or faster by different mixing ratio or room temperature), we
advice you de-mold after 24 hours, it is will improve the replicate
times of silicone mold.
Packing
20kg/drum, 25kg/drum or 200kg/drum of Part A base silicone
0.8kg/bottle of Part B CA30-10 Curing Agent
STORAGE
When stored at or below 30 C (85F) in the original unopened
containers, MC silicone RTV9920 Base and CA30-10 Curing agent have
a usable life of 10 months from the date of production. After 10
months stock, please use the Stir to mixing the Part A silicone for
some minutes, then the silicone can be use again, no influence for
other performance.
Note:
Silicone RTV930 is an industrial product and must not be used in
food molding, dental human skin molding applications.
Temperature resistance range: -50~200 °C