Two Part Platinum Cured Liquid Silicone Rubbers Translucent
Silicone For Candle & Soap Molds 10 Shore A
Product description
MCPLA-L10 is a high-performing line of room-temperature curing
(RTV), two-part, platinum-cured silicone rubbers designed for the
manufacture of flexible molds.the platinum molds have excellent
release properties and are suitable for casting a number of
materials.Platinum silicone rubbers exhibit no shrink on cure and have long
library life.
Features
Outstanding release properties
Curing can be heat accelerated
Very low shrinkage and good dimensional stability
Can be used for high temperature casting applications
Applications
1. A range of materials can be cast into the cured silicone mold:
polyurethane and other reactive resins
Small pieces of cement,plaster,concrete products.
Food like chocolate,fondants
Wax,candle,soap;
Processing and Instructions of Addition Cure Silicones
1. Mixing the two components
According the mixing ration 10:1 weighting A and B, the two
components may be thoroughly mixed either by hand or using a
low-speed electric to minimize the degassing of bubbles and to
avoid any temperature increase.
Note: It is also possible to use a special mixing and dispensing
machine for the silicone components, further information is
available upon request.
2. Moulding
The mixture should be degassed preferably at 30 to 50 mbar to
eliminate any entrapped air. If a dispensing machine is used, the
two components are degassed separately prior to mixing. The
silicone mixture expands to 3-4 times of its initial volume and
bubbles rise to the surface. The bubbles progressively disappear
and the mixture returns to its initial volume after 5 to 10
minutes. Wait a few minutes to complete the degassing and then
flash the vacuum. The silicone is ready for pouring, either by
gravity or under low pressure.
Note: Flashing the vacuum once or twice accelerates the degassing.
It is recommended to use a container with a high diameter/height
ratio (3 to 4 times of the initial volume)
3. Polymerisation
The curing may be slowed down at lower temperature or accelerated
by applying heat.
Note:
1. Contamination from sulfur (e.g., sulfur-based clay), amines, tin
compounds, cured polyester resin, some paints and some silicone
rubbers may inhibit surface cure of platinum-cured rubbers.
2. Apply a release agent, Although not usually necessary, a release
agent will make demolding easier when casting into most surfaces.
Packaging
20kg per drum, 200kg per drum
Storage and shelf life
When the silicone rubber is stored at or below 25 degree Celsius in
the original unopened containers, Silicone Base and Curing agent
have a usable life of 12 months from the date of production. After
12 months’ stockpiles, please use tool to stir the Part A silicone
for some minutes, then the silicone can be use again, no influence
for other performance.
1. Store the original packing tightly sealed and at a temperature
below 25 degree Celsius.Use the product as soon as the packaging
has been opened.
2. Close the lid tightly after taking out the proper amount of
liquid silicone rubber.
Use the product as soon as the packaging has been opened.